ASTM Corten A Corten B Corten Steel Plak
| ASTM Corten Yon konpozisyon chimik dezagregasyon asye | |||||||||
|---|---|---|---|---|---|---|---|---|---|
| Klas | C Max | SIZO | Mn | S Max | Kr | Ni | Taks | Nòb | Nb+V=Ti |
| Corten A | 0.12 | 0.25-0.75 | 0.20-0.50 | 0.07-0.15 | 0.030 | 0.50-1.25 | 0.65 | 0.25-0.55 | - |
| ASTM Corten Yon materyèl corten Pwopriyete mekanik | |||||
|---|---|---|---|---|---|
| Klas | Pwen sede akseptab rapò |
Sede fòs MPa (min) |
Fòs rupture MPa |
Elongasyon % (min) |
Bend |
| Corten A | - | 355 | 470-630 | 20 | 1t |
| Corten Yon corten dezagregasyon asye Weathering Steel Paramèt | ||||||||
|---|---|---|---|---|---|---|---|---|
| Rekòmande koube reyon san kondisyon espesyal | ||||||||
| Epesè mm | 2-3 | 4 | 5 | 6 | 7 | 8 | 10 | 12 |
| Reyon mm | 4 | 8 | 10 | 12 | 21 | 24 | 30 | 36 |
| ASTM Corten B dezagregasyon plak konpozisyon chimik | ||
|---|---|---|
| Klas / Materyèl | Eleman | Konpozisyon (Max-A, Min-I) |
| Corten B | C | A: 0.19 |
| Mn | 0.30-0.65 | |
| sizo | 0.80-0.25 | |
| P | A:0.035 | |
| S | A:0.030 | |
| al | 0.020-0.06 | |
| V | 0.02-0.10 | |
| Taks | 0.25-0.40 | |
| Kr | 0.40-0.65 | |
| Ni | 0.40 | |
| ASTM Corten B plak corten asye Pwopriyete mekanik | ||
|---|---|---|
| Klas/Materyèl | Tès Tensile | Ksi/MPa |
| Corten B | Fòs rupture | I:485 |
| Sede fòs | I:345 | |
| Elongasyon | 19% | |
| Tès enpak (si genyen) | ||
Baj popilè: move tan ki reziste plak asye, Lachin dezagregasyon ki reziste plak asye manifaktirè, Swèd, faktori