AH40 plak asyese sitou itilize pou konstriksyon bato ak platfòm lwil oliv, klas konstriksyon bato AH40 ka itilize nan envantè estrikti ekòs bato a, ki gen pwa se plis pase 10000 tòn. Klas konstriksyon bato AH40 se asye a segondè fòs rupture, AH40 asye pou konstriksyon bato ak platfòm lwil oliv dwe bon pwopriyete severite, pi wo fòs, fò korozyon-rezistans, pwopriyete yo pwosesis, ak pwopriyete soude.
AH40 spesifikasyon plak asye konstriksyon bato:
Epesè: 6mm-200mm, Lajè: 1500mm-4000mm, Longè: 6000mm-180000mm
ABS Klas AH40 Shipbuilding Steel Plak Konpozisyon Chimik ak Pwopriyete Mekanik
| C max | Si max | Mn | P max | S max | Als | Nb | V | Ti max. | Cu max. | Cr max. | Ni max. | Mo max. | N max. |
|
0.18 |
0.50 | 0.90-1.60 |
0.030 |
0.030 |
0.015 | 0.02-0.05 | 0.05-0.10 | 0.02 | 0.35 | 0.20 | 0.40 | 0.08 |
- |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 390 | 510-660 | 20 |
ABS Klas DH40 plak asye konstriksyon bato
GNEE Steel ka bay ABS klas DH40 plak asye konstriksyon bato / plak asye maren, sitou itilize nan konstriksyon pou bato.
Gwosè Pwodiksyon: Epesè: 4mm- 200mm; Lajè: 1000mm- 4000mm; Longè: 4000mm- 12000mm.
Kapasite pwodiksyon: 10000 tòn pa mwa.
Fason Pwodiksyon: Cho woule
Detay teknik:
Tretman Chalè: Nòmalize, Trempe, Tanperaman, Tès Enpak, .. (Opsyonèl si yo pa bay règ yo)
|
Klas / Materyèl |
Eleman |
Konpozisyon (Max-A, Min-I) |
|
ABS Klas DH40/ ABS DH40 |
C |
0.18 |
|
Mn |
0.90- 1.60 |
|
|
Si |
0.10- 0.50 |
|
|
P |
0.035 |
|
|
S |
0.035 |
Konpozisyon chimik (%):
Pwopriyete mekanik (Mpa)
|
Klas / Materyèl |
Tès Tensile |
Ksi/MPa |
|
ABS Klas DH40/ ABS DH40 |
Fòs rupture |
74-94/ 490-620 |
|
Sede fòs |
57/ 390 |
|
|
Elongasyon |
I: 19% |
|
|
Tès enpak (si genyen) |
-20 degre |
ABS Klas EH40 Shipbuilding Steel Plak Konpozisyon Chimik ak Pwopriyete Mekanik
| C max | Si max | Mn | P max | S max | Als | Nb | V | Ti max. | Cu max. | Cr max. | Ni max. | Mo max. | N max. |
|
0.18 |
0.50 | 0.90-1.60 |
0.025 |
0.025 |
0.015 | 0.02-0.05 | 0.05-0.10 | 0.02 | 0.35 | 0.20 | 0.40 | 0.08 |
- |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 390 | 510-660 | 20 |
ABS Klas FH40 Shipbuilding Steel Plak Konpozisyon Chimik ak Pwopriyete Mekanik
| C max | Si max | Mn | P max | S max | Als | Nb | V | Ti max. | Cu max. | Cr max. | Ni max. | Mo max. | N max. |
|
0.16 |
0.50 | 0.90-1.60 |
0.020 |
0.0.20 |
0.015 | 0.02-0.05 | 0.05-0.10 | 0.02 | 0.35 | 0.20 | 0.80 | 0.08 |
0.009 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 390 | 510-660 | 20 |