Gen kat nivo kalite plak bato: A, D, E, ak F, ki koresponn ak tanperati enpak respektivman.
A pa afekte,
D enpak tanperati -20 degre enpak,
E se plak asye -40 enpak degre,
F se enpak -60 degre plak asye a,
H endike ke plak asye a se yon plak asye wo-fòs, ak 32 endike fòs la konpresiv nan plak la asye.
Plak asye FH32 se yon plak asye ki itilize pou enpak ba-tanperati nan -60 degre pou estrikti ekòs. Ka klas asye plak la ka kraze nan, F enpak tanperati -60 degre enpak. Plak asye FH32 se yon asye touye amann ki pwodui dapre estanda sosyete klasifikasyon an.
GL klas AH32 Shipbuilding Steel plak konpozisyon chimik ak pwopriyete mekanik
| C max | Si max | Mn | P max | S max | Als | Nòb | V | Ti max. | Cu max. | Cr max. | Ni max. | Mo max. | N max. |
|
0.18 |
0.50 | 0.90-1.60 |
0.030 |
0.0.30 |
0.015 | 0.02-0.05 | 0.05-0.10 | 0.02 | 0.35 | 0.20 | 0.40 | 0.08 |
- |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 315 | 450-570 | 22 |
GL klas DH32 Shipbuilding Steel plak konpozisyon chimik ak pwopriyete mekanik
| C max | Si max | Mn | P max | S max | Als | Nòb | V | Ti max. | Cu max. | Cr max. | Ni max. | Mo max. | N max. |
|
0.18 |
0.50 | 0.90-1.60 |
0.025 |
0.0.25 |
0.015 | 0.02-0.05 | 0.05-0.10 | 0.02 | 0.35 | 0.20 | 0.40 | 0.08 |
- |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 315 | 450-570 | 22 |
GL Grade EH32 Shipbuilding Steel Plak Konpozisyon chimik ak pwopriyete mekanik
| C max | Si max | Mn | P max | S max | Als | Nòb | V | Ti max. | Cu max. | Cr max. | Ni max. | Mo max. | N max. |
|
0.18 |
0.50 | 0.90-1.60 |
0.025 |
0.025 |
0.015 | 0.02-0.05 | 0.05-0.10 | 0.02 | 0.35 | 0.20 | 0.40 | 0.08 |
- |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 315 | 450-570 | 22 |
GL klas FH32 Shipbuilding Steel plak konpozisyon chimik ak pwopriyete mekanik
| C max | Si max | Mn | P max | S max | Als | Nòb | V | Ti max. | Cu max. | Cr max. | Ni max. | Mo max. | N max. |
|
0.16 |
0.50 | 0.90-1.60 |
0.020 |
0.0.20 |
0.015 | 0.02-0.05 | 0.05-0.10 | 0.02 | 0.35 | 0.20 | 0.80 | 0.08 |
0.009 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 315 | 450-570 | 22 |