Plak asye GL bato klas / plak asye bato / platfòm oseyan
Klas Plak asye GL Ship Class:
GL A420 GL D420 GL E420 GL F420
GL A460 GL D460 GL E460 GL F460
GL A500 GL D500 GL E500 GL F500
GL A550 GL D550 GL E550 GL F550
GL A620 GL D620 GL E620 GL F620
GL A690 GL D690 GL E690 GL F690
GL Ship Class Steel Plate Production Size:
Epesè: 4mm- 200mm;
Lajè: 1000mm- 4000mm;
Longè: 4000mm- 12000mm.
Kapasite pwodiksyon:
100000 tòn pa mwa.
Fason pwodiksyon:
Woule cho
Kondisyon teknik ak sèvis adisyonèl pou plak asye klas bato GL GL:
♦ Tès tansyon wo
♦ Z-Tès (Z15,Z25,Z35)
♦ Ba tanperati enpak tès
♦ Piki eksplozif ak Penti, Koupe ak soude dapre demann itilizatè final la
GL Klas A420 Konstriksyon Asye Plak Konpozisyon Chimik ak Pwopriyete Mekanik
| C max | Si max | Mn | P max | S max | N max. |
|
0.21 |
0.55 | 1.70 |
0.030 |
0.030 |
0.020 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 420 | 530-680 | 18 |
GL klas D420 Shipbuilding Steel plak konpozisyon chimik ak pwopriyete mekanik
| C max | Si max | Mn | P max | S max | N max. |
|
0.20 |
0.55 | 1.70 |
0.025 |
0.025 |
0.020 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 420 | 530-680 | 18 |
GL klas E420 Shipbuilding Steel plak konpozisyon chimik ak pwopriyete mekanik
| C max | Si max | Mn | P max | S max | N max. |
|
0.20 |
0.55 | 1.70 |
0.025 |
0.025 |
0.020 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 420 | 530-680 | 18 |
GL Klas F420 Konstriksyon Asye Plak Konpozisyon Chimik ak Pwopriyete Mekanik
| C max | Si max | Mn | P max | S max | N max. |
|
0.18 |
0.55 | 1.60 |
0.020 |
0.020 |
0.020 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 420 | 530-680 | 18 |
GL klas A460 Shipbuilding Steel plak konpozisyon chimik ak pwopriyete mekanik
| C max | Si max | Mn | P max | S max | N max. |
|
0.21 |
0.55 | 1.70 |
0.030 |
0.030 |
0.020 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 460 | 570-720 | 17 |
GL Grade D460 konstriksyon bato asye plak konpozisyon chimik ak pwopriyete mekanik
| C max | Si max | Mn | P max | S max | N max. |
|
0.20 |
0.55 | 1.70 |
0.025 |
0.025 |
0.020 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 460 | 570-720 | 17 |
GL klas E460 Shipbuilding Steel plak konpozisyon chimik ak pwopriyete mekanik
| C max | Si max | Mn | P max | S max | N max. |
|
0.20 |
0.55 | 1.70 |
0.025 |
0.025 |
0.020 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 460 | 570-720 | 17 |
GL Klas F460 Konstriksyon Asye Plak Konpozisyon Chimik ak Pwopriyete Mekanik
| C max | Si max | Mn | P max | S max | N max. |
|
0.18 |
0.55 | 1.60 |
0.020 |
0.020 |
0.020 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 460 | 570-720 | 17 |
GL klas A500 Shipbuilding Steel plak konpozisyon chimik ak pwopriyete mekanik
| C max | Si max | Mn | P max | S max | N max. |
|
0.21 |
0.55 | 1.70 |
0.030 |
0.030 |
0.020 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 500 | 610-770 | 16 |
GL klas D500 Shipbuilding Steel plak konpozisyon chimik ak pwopriyete mekanik
| C max | Si max | Mn | P max | S max | N max. |
|
0.20 |
0.55 | 1.70 |
0.025 |
0.025 |
0.020 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 500 | 610-770 | 16 |
GLKlas E500 konstriksyon bato asye plak konpozisyon chimik ak pwopriyete mekanik
| C max | Si max | Mn | P max | S max | N max. |
|
0.20 |
0.55 | 1.70 |
0.025 |
0.025 |
0.020 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 500 | 610-770 | 16 |
GL Klas F500 Konstriksyon Asye Plak Konpozisyon Chimik ak Pwopriyete Mekanik
| C max | Si max | Mn | P max | S max | N max. |
|
0.18 |
0.55 | 1.60 |
0.020 |
0.020 |
0.020 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 500 | 610-770 | 16 |
GL klas A550 Shipbuilding Steel plak konpozisyon chimik ak pwopriyete mekanik
| C max | Si max | Mn | P max | S max | N max. |
|
0.21 |
0.55 | 1.70 |
0.030 |
0.030 |
0.020 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 550 | 670-830 | 16 |
GL klas D550 Shipbuilding Steel plak konpozisyon chimik ak pwopriyete mekanik
| C max | Si max | Mn | P max | S max | N max. |
|
0.20 |
0.55 | 1.70 |
0.025 |
0.025 |
0.020 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 550 | 670-830 | 16 |
GL klas E550 Shipbuilding Steel plak konpozisyon chimik ak pwopriyete mekanik
| C max | Si max | Mn | P max | S max | N max. |
|
0.20 |
0.55 | 1.70 |
0.025 |
0.025 |
0.020 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 550 | 670-830 | 16 |
GLKlas F550 Shipbuilding Steel Plak konpozisyon chimik ak pwopriyete mekanik
| C max | Si max | Mn | P max | S max | N max. |
|
0.18 |
0.55 | 1.60 |
0.020 |
0.020 |
0.020 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 550 | 670-830 | 16 |
GL klas A620 Shipbuilding Steel plak konpozisyon chimik ak pwopriyete mekanik
| C max | Si max | Mn | P max | S max | N max. |
|
0.21 |
0.55 | 1.70 |
0.030 |
0.030 |
0.020 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 620 | 720-890 | 15 |
GL klas D620 Shipbuilding Steel plak konpozisyon chimik ak pwopriyete mekanik
| C max | Si max | Mn | P max | S max | N max. |
|
0.20 |
0.55 | 1.70 |
0.025 |
0.025 |
0.020 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 620 | 720-890 | 15 |
GL klas E620 Shipbuilding Steel plak konpozisyon chimik ak pwopriyete mekanik
| C max | Si max | Mn | P max | S max | N max. |
|
0.20 |
0.55 | 1.70 |
0.025 |
0.025 |
0.020 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 620 | 720-890 | 15 |
GL Klas F620 Konstriksyon Asye Plak Konpozisyon Chimik ak Pwopriyete Mekanik
|
Klas |
Konpozisyon chimik (%) |
||||
|
C |
Mn Greater than or equal to |
sizo |
P |
S |
|
|
GL F620 |
0.18 |
0.90-1.60 |
0.10-0.50 |
0.035 |
0.035 |
|
Klas |
Pwopriyete mekanik |
|
|||
|
Fòs rupture (MPa) |
Sede fòs (MPa) |
% elongasyon nan 2 pous (50mm) min |
Konsekans Tanperati Tès (degre) |
|
|
|
GL F620 |
400-590 |
315 |
22 |
-20 |
|
GL klas A690 Shipbuilding Steel plak konpozisyon chimik ak pwopriyete mekanik
| C max | Si max | Mn | P max | S max | N max. |
|
0.21 |
0.55 | 1.70 |
0.030 |
0.030 |
0.020 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 690 | 770-940 | 14 |
GL klas D690 Shipbuilding Steel plak konpozisyon chimik ak pwopriyete mekanik
| C max | Si max | Mn | P max | S max | N max. |
|
0.20 |
0.55 | 1.70 |
0.025 |
0.025 |
0.020 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 690 | 770-940 | 14 |
GL klas E690 Shipbuilding Steel plak konpozisyon chimik ak pwopriyete mekanik
| C max | Si max | Mn | P max | S max | N max. |
|
0.20 |
0.55 | 1.70 |
0.025 |
0.025 |
0.020 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 690 | 770-940 | 14 |
GL klas F690 Shipbuilding Steel plak konpozisyon chimik ak pwopriyete mekanik
| C max | Si max | Mn | P max | S max | N max. |
|
0.18 |
0.55 | 1.60 |
0.020 |
0.020 |
0.020 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 690 | 770-940 | 14 |