RINA bato klas siplemantè segondè fòs asye klas:
RINA A420, RINA D420, RINA E420, RINA F420
RINA A460, RINA D460, RINA E460, RINA F460
RINA A500, RINA D500, RINA E500, RINA F500
RINA A550, RINA D550, RINA E550, RINA F550
RINA A620, RINA D620, RINA E620, RINA F620
RINA A690, RINA D690, RINA E690, RINA F690
RINA Ship Plate Z Test:Z15,Z25,Z35
RINA Shipbuilding Steel Plate Size:
Epesè: 4mm a 200mm
Lajè: 1500mm a 4000mm
Longè: 4000mm a 27000mm
RINA bato klas siplemantè segondè fòs asye klas konpozisyon chimik ak pwopriyete mekanik:
RINA klas A420 Shipbuilding Steel plak konpozisyon chimik ak pwopriyete mekanik
| C max | Si max | Mn | P max | S max | N max. |
|
0.21 |
0.55 | 1.70 |
0.030 |
0.030 |
0.020 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 420 | 530-680 | 18 |
RINA klas D420 konstriksyon bato asye plak konpozisyon chimik ak pwopriyete mekanik
| C max | Si max | Mn | P max | S max | N max. |
|
0.20 |
0.55 | 1.70 |
0.025 |
0.025 |
0.020 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 420 | 530-680 | 18 |
RINA klas E420 konstriksyon bato asye plak konpozisyon chimik ak pwopriyete mekanik
| C max | Si max | Mn | P max | S max | N max. |
|
0.20 |
0.55 | 1.70 |
0.025 |
0.025 |
0.020 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 420 | 530-680 | 18 |
RINA klas F420 konstriksyon bato asye plak konpozisyon chimik ak pwopriyete mekanik
| C max | Si max | Mn | P max | S max | N max. |
|
0.18 |
0.55 | 1.60 |
0.020 |
0.020 |
0.020 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 420 | 530-680 | 18 |
RINA klas A460 Shipbuilding Steel plak konpozisyon chimik ak pwopriyete mekanik
| C max | Si max | Mn | P max | S max | N max. |
|
0.21 |
0.55 | 1.70 |
0.030 |
0.030 |
0.020 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 460 | 570-720 | 17 |
RINA klas D460 konstriksyon bato asye plak konpozisyon chimik ak pwopriyete mekanik
| C max | Si max | Mn | P max | S max | N max. |
|
0.20 |
0.55 | 1.70 |
0.025 |
0.025 |
0.020 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 460 | 570-720 | 17 |
RINA klas E460 Shipbuilding Steel plak konpozisyon chimik ak pwopriyete mekanik
| C max | Si max | Mn | P max | S max | N max. |
|
0.20 |
0.55 | 1.70 |
0.025 |
0.025 |
0.020 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 460 | 570-720 | 17 |
RINA klas F460 Shipbuilding Steel plak konpozisyon chimik ak pwopriyete mekanik
| C max | Si max | Mn | P max | S max | N max. |
|
0.18 |
0.55 | 1.60 |
0.020 |
0.020 |
0.020 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 460 | 570-720 | 17 |
RINA klas A500 konstriksyon bato asye plak konpozisyon chimik ak pwopriyete mekanik
| C max | Si max | Mn | P max | S max | N max. |
|
0.21 |
0.55 | 1.70 |
0.030 |
0.030 |
0.020 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 500 | 610-770 | 16 |
RINA klas D500 konstriksyon bato asye plak konpozisyon chimik ak pwopriyete mekanik
| C max | Si max | Mn | P max | S max | N max. |
|
0.20 |
0.55 | 1.70 |
0.025 |
0.025 |
0.020 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 500 | 610-770 | 16 |
RINA klas E500 konstriksyon bato asye plak konpozisyon chimik ak pwopriyete mekanik
| C max | Si max | Mn | P max | S max | N max. |
|
0.20 |
0.55 | 1.70 |
0.025 |
0.025 |
0.020 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 500 | 610-770 | 16 |
RINA klas F500 konstriksyon bato asye plak konpozisyon chimik ak pwopriyete mekanik
| C max | Si max | Mn | P max | S max | N max. |
|
0.18 |
0.55 | 1.60 |
0.020 |
0.020 |
0.020 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 500 | 610-770 | 16 |
RINA klas A550 Shipbuilding Steel plak konpozisyon chimik ak pwopriyete mekanik
| C max | Si max | Mn | P max | S max | N max. |
|
0.21 |
0.55 | 1.70 |
0.030 |
0.030 |
0.020 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 550 | 670-830 | 16 |
RINA klas D550 konstriksyon bato asye plak konpozisyon chimik ak pwopriyete mekanik
| C max | Si max | Mn | P max | S max | N max. |
|
0.20 |
0.55 | 1.70 |
0.025 |
0.025 |
0.020 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 550 | 670-830 | 16 |
RINA klas E550 Shipbuilding Steel plak konpozisyon chimik ak pwopriyete mekanik
| C max | Si max | Mn | P max | S max | N max. |
|
0.20 |
0.55 | 1.70 |
0.025 |
0.025 |
0.020 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 550 | 670-830 | 16 |
RINA klas F550 Shipbuilding Steel plak konpozisyon chimik ak pwopriyete mekanik
| C max | Si max | Mn | P max | S max | N max. |
|
0.18 |
0.55 | 1.60 |
0.020 |
0.020 |
0.020 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 550 | 670-830 | 16 |
RINA klas A620 konstriksyon bato asye plak konpozisyon chimik ak pwopriyete mekanik
| C max | Si max | Mn | P max | S max | N max. |
|
0.21 |
0.55 | 1.70 |
0.030 |
0.030 |
0.020 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 620 | 720-890 | 15 |
RINA klas D620 konstriksyon bato asye plak konpozisyon chimik ak pwopriyete mekanik
| C max | Si max | Mn | P max | S max | N max. |
|
0.20 |
0.55 | 1.70 |
0.025 |
0.025 |
0.020 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 620 | 720-890 | 15 |
RINA Klas E620 Shipbuilding Steel Plak Konpozisyon Chimik ak Pwopriyete Mekanik
| C max | Si max | Mn | P max | S max | N max. |
|
0.20 |
0.55 | 1.70 |
0.025 |
0.025 |
0.020 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 620 | 720-890 | 15 |
RINA klas F620 konstriksyon bato asye plak konpozisyon chimik ak pwopriyete mekanik
| C max | Si max | Mn | P max | S max | N max. |
|
0.18 |
0.55 | 1.60 |
0.020 |
0.020 |
0.020 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 620 | 720-890 | 15 |
RINA klas A690 Shipbuilding Steel plak konpozisyon chimik ak pwopriyete mekanik
| C max | Si max | Mn | P max | S max | N max. |
|
0.21 |
0.55 | 1.70 |
0.030 |
0.030 |
0.020 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 690 | 770-940 | 14 |
RINA klas D690 konstriksyon bato asye plak konpozisyon chimik ak pwopriyete mekanik
| C max | Si max | Mn | P max | S max | N max. |
|
0.20 |
0.55 | 1.70 |
0.025 |
0.025 |
0.020 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 690 | 770-940 | 14 |
RINA klas E690 Shipbuilding Steel Plak konpozisyon chimik ak pwopriyete mekanik
|
Klas |
Konpozisyon chimik (%) |
||||
|
C |
Mn Greater than or equal to |
Si |
P |
S |
|
|
RINA E690 |
0.21 |
1.70 |
0.10-0.55 |
0.035 |
0.035 |
|
Klas |
Pwopriyete mekanik |
|
|||
|
Fòs rupture (MPa) |
Sede fòs (MPa) |
% elongasyon nan 2 pous (50mm) min |
Konsekans Tanperati Tès (degre) |
|
|
|
RINA E690 |
770-940 |
690 |
18 |
-40 |
|
RINA klas F690 konstriksyon bato asye plak konpozisyon chimik ak pwopriyete mekanik
| C max | Si max | Mn | P max | S max | N max. |
|
0.18 |
0.55 | 1.60 |
0.020 |
0.020 |
0.020 |
| Fòs Sede (MPa) min. | Fòs rupture (MPa) | Pwolonjman min. % |
| 690 | 770-940 | 14 |