1. Efè tanperati chofaj
(a) Optimal (850-1050 degre)
Microstructure: Inifòm austenit (mou, ductile, ideyal pou deformation).
Pwopriyete: Fasil pou fòje/woule; Post - Ferit refwadisman - Pearlite Microstructure asire balanse fòs (pi gran pase oswa egal a 345 MPa) ak andirans. CR/CU fonn respire, konsève rezistans move tan.
(b) Stremperature (<850°C)
Microstructure: Enkonplè austenitization (rezidyèl ferit difisil/Pearlite).
Pwopriyete: Pòv pratik (tendans fann); Fòs inegal/severite.
(c) Overheating (>1050 degre)
Microstructure: Austenit koryas; CR/CU separe nan limit grenn jaden.
Pwopriyete: Redwi severite (grenn koryas); fòmasyon paten inegal (rezistans move tan febli); Echèl sifas/decarburizasyon.
2. Efè to refwadisman
(a) Ralanti (lè/gwo fou refwadisman - estanda)
Microstructure: Fine ferit - Pearlite.
Pwopriyete: Balanse fòs/duktilite (elongasyon pi gran pase oswa egal a 20%); segondè severite; menm CR/CU distribisyon (ki konsistan rezistans move tan).
(b) medyòm (fòse lè)
Microstructure: Ferit - Bainite (grenn sibtilite).
Pwopriyete: Pi wo fòs (400-450 MPa); yon ti kras pi ba duktilite; Rezistans kenbe.
(c) rapid (dlo quenching - raman itilize)
Microstructure: Frajil martensit.
Pwopriyete: Ekstrèm dite men tou pre - zewo duktilite (tendans fann); Pòv weldability; Estrès risk korozyon.